D2/D2V.80/1.2379

Tool Steels

Tool and Die Steel Includes Cold Work Steel, Hot Work Steel, Plastic Mould Steel, High Speed Steel. These tool materials adhere to great quality demands of steel like temper, strength, toughness, resistance to tempering, hardening capacity, dimensional stability etc. The range of Tool Steel in our store includes products from renowned manufacturers.

Main characteristics and applications

Threading rolls and dies, cold extrusion tools, trimming, cutting and stamping tools for sheet thicknesses up to 6 mm, precision cutting tools for sheet thicknesses up to 12 mm, cold pilger mandrels, circular-shear blades, deep-drawing tools, pressure pads and highly wear-resistant plastic moulds.

Steel properties

12 % ledeburitic chromium steel. Combines maximum wear resistance, good toughness, outstanding cutting edge retention and tempering resistance. It can be nitrided after special heat treatment.

Comparable standards

DIN	W.Nr	AFNOR	AISI/ASIM	JIS
X155CrVMo12-1	1.2379	Z160CDV12	D-2	SKD11

Chemical composition (typical; in weight %)

C	Si	Mn	P(Max)	S(Max)	Ci	Mo	V
1.45-1.60	0.10-0.60	0.20-0.60	0.03	0.03	11.0-13.0	0.70-1.00	0.70-1.00

Physical properties (reference values)

	20°C	100°C	200°C	500°C
Coefficient of thermal expansion at °C 10-6 m/(W/mk)	10.5	11.5		12.2
Thermal conductivity at °C (W/mk)	16.7	20.5

Heat treatment

TREATMENT	TEMPERATURE	HOLDING TIME (HT)	COOLING	COMMENTS
Annealing	Heat to 830 – 860 °C	Min. H.T. for 2 minute /mm	Furnace	-
Stress relieving	Heat to 650 – 700 °C	Min. H.T. for 2 minute /mm	Furnace	-
Hardening	Heat to 1000 – 1050 °C	Min. H.T. for 1 minute /mm	Air, oil or saltbath, 500 – 550 °C	-

Note
Hardening temperature 1050-1080 °C, tempered 3 times

°C	100	200	300	400	500	525	550	600
HRC	63	61	58	58	58	60	56	50